In-situ TiB2 particles reinforced 2014 aluminum alloy composite was prepared using an exothermic reaction process with K2TiF6 and KBF4 salts. The effects of CeO2 additive on the microstructure and properties of in-situ TiB2/2014 composite were investigated. The results showed that CeO2 at high temperature exhibits the same function as Ce. When 0.5% （mass fraction） CeO2 additive was added, the dispersion of TiB2 particles in the matrix is improved significantly, and particles have no obvious settlement. The dispersing mechanism of TiB2 particles in 2014 Al alloy matrix was explained. Compared with the composite without CeO2, the hardness, tensile strength, yield strength and elongation of the composite with CeO2 addition are greatly increased in as-cast condition.