Asphalt mixture is the most widely used pavement material all over the world. In China, more than 90% of service expressways are asphalt pavement. However, current asphalt pavement design method still has irrationality. Even though maximum tensile stress theory is used as failure criterion, pavement structure under the effects of wheel load is in three-dimensional complex stress state. Obviously, one-dimensional strength theory cannot reflect the failure characteristics and the resistance of pavement structure. So it is necessary to study the failure criterion of asphalt mixture under three-dimensional com- plex stress state. Due to limitations of test equipment, there are almost no studies in related area. Under this background, this paper develops a new triaxial test method, ac- cording to the investigation of strength characteristics of asphalt mixture under complex stress state through plane isobaric/axial tensile test, plane isobaric/axial compression test, plane tensile and compression/axial tensile test, to reveal the general rules of asphalt mixture＇s strength failure. The failure mode is divided into three types： tensile failure, shear failure and rheological failure. The tensile meridian and compression meridian in the stress space and strength envelope in the π plane where hydrostatic pressure is greater than zero are obtained, and the failure criterion of asphalt mixture under complex stress state is established, providing theoretical method and scientific basis for structure design as well as strength check of asphalt pavement under three-dimensional stress state.
为了得到老化对沥青混合料疲劳寿命的影响规律,通过对SHRP沥青混合料长期老化试验方法的改进,提出了对沥青混合料进行长期老化的试验方法,利用MTS(Material Test System-810)进行了不同老化程度下的疲劳试验,通过对疲劳试验结果的分析,得到了不同老化程度下的沥青混合料S-N疲劳方程,为分析老化对沥青混合料疲劳特性的影响提供了依据。分析结果表明:老化并不改变沥青混合料S-N疲劳方程在双对数坐标系中的线性关系,随着老化程度的增加,其疲劳耐久性变得越来越差,因此在沥青路面施工及运营过程中应采取适当措施减少或延缓其老化。